Gaz himoyalangan arc misli pering sim er70s-6, SG2 payvandlash simlari
Missiz payvandlash simini joriy etish:
Faol nanometrning faol texnologiyasidan so'ng, mis miqdori, piksozlik bo'yicha piksozlik, peldalashning chuqurligi, peldalashning tezligi, peldali payvandlashning chuqurligi juda yaxshilandi. Tutun. Yangi yuzani davolash usulini ishlab chiqish, misga qarshi zangga qarshi xususiyatorda misga qarshi turmadan ustundir.
1. Atrofli yoy.
2. Kampir zarralari kamroq
3. Sovutorli simlarni boqish xususiyati.
4.GUS ERCni cheklash
5.Gan zangga qarshi mulkni payvandlash simining yuzasida.
6. Mis chekish hosil qiladi.
7. Hozirgi aloqani kamroq tuting.
Ehtiyot choralari:
1. Payvandlash jarayoni parametrlari payvand metallining mexanik xususiyatlariga ta'sir qiladi va foydalanuvchi payvandlash jarayoni malakasini amalga oshirishi kerak.
2. Payvandlash zonasida zang, nam, neft, chang va boshqa aralashmalar payvandlashdan oldin ehtiyotkorlik bilan olib tashlanishi kerak.
Texnik xususiyatlar:Diametri: 0,8mm, 0,9mm, 1,0 mm, 1,2mm, 1,3 mm, 1,6 mm, 2.,0 mm
Qadoqlash hajmi: uchun 15kg / 20 kg.
Payvandlash simining odatiy kimyoviy tarkibi(%)
==========================================
| Element | C | Mn | Si | S | P | Ni | Cr | Mo | V | Cu |
| Talab | 0.06-0.15 | 1.40-1.85 | 0.80-1.15 | ≤0.025 | ≤0.025 | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.03 | ≤0.50 |
| Haqiqiy avg natijasi | 0,08 | 1.45 | 0,85 | 0,007 | 0.013 | 0.018 | 0.034 | 0,06 | 0.012 | 0,28 |
Omonatlangan metallning odatiy mexanik xususiyatlari
========================================
| Sinov element | Mustahkamlik chegarasi RM (MPA) | Kuch berish kuchi RM (MPA) | Cho'zish A (%) | V model Bump testi | |
| Sinov tempi (ºC) | Ta'sir qiymati (J) | ||||
| Talablar | ≥500 | ≥420 | ≥22 | -30 | ≥27 |
| Haqiqiy avg natijasi | 589 yil | 490 | 26 | -30 | 79 |
Hajmi va tavsiya etilgan joriy diapazon.
===============================
| Diametri | 0,8mm | 0.9mm | 1.,0 mm | 1.2 mm | 1.6 mm | 1.6 mm |
| Amp | 50-140 | 50-200 | 50-220 | 80-350 | 120-450 | 120-300 |